Physical activation and characterization of tannin-based foams enforced with boric acid and zinc chloride
2019
In this study, tannin-furanic-based foams enforced with H3BO3 and ZnCl2 are investigated, as well as their properties such as mechanical strength, specific surface area, and pore size distribution. From an industrial point of view, the aforementioned properties of these foams play a key role when used as catalyst, adsorbent, or gas storing materials. Therefore, this study aims to prove that such enforced tannin-furanic foams are promising materials for these types of applications. According to the results, materials that are up to five times stronger can be achieved by carbonizing the foams in comparison to maturing them. With physical activation, it was possible to obtain a specific surfac…
Catalytic effect of transition metals (copper, iron, and nickel) on the foaming and properties of sugar-based carbon foams
2019
Abstract Recently, bio-based carbon foams have gained much interest in many chemical industry fields because of their unique structure and properties. This study provides new information on the effects of catalytic metals (iron, nickel, and copper) on the foaming process. Specifically, the effects of these catalysts on the density, foam growth, and cell size and then further on the pore size distribution and specific surface areas after the physical activation are considered. Furthermore, some of the activated sugar foams were used in adsorption tests using methylene blue as adsorbent. Results showed that the highest effect on foam density was obtained using the iron catalyst in the foaming…
Activated carbon from hydrolysis lignin: Effect of activation method on carbon properties
2022
This study presents the effects of different activation methods to produce activated carbon from the hydrolysis lignin. Pretreatment of the feedstock with common mineral acids (HCL, HNO3, and H3PO4), different steam rates for physical activation, and different chemical activating agents (ZnCl2, Na2CO3, and KOH) for chemical activation were investigated. The pretreated biomass was carbonized and activated in one-stage process and the surface characteristics, such as total pore volume, pore size distribution and specific surface area, were investigated. The results showed that the activated carbon surface properties were not greatly affected by acid pretreatment. Brunauer-Emmett-Teller (BET) …
Comparison of the Properties of Activated Carbons Produced in One-Stage and Two-Stage Processes
2018
Activated carbons (ACs) can be produced from biomass in a thermal process either in a direct carbonization-activation process or by first carbonizing the biomass and later activating the bio-chars into activated carbons. The properties of the ACs are dependent on the type of process used for production. In this study, the properties of activated carbons produced in one-stage and two-stage processes are considered. Activated carbons were produced by physical activation of two types of starting materials: bio chars produced from spruce and birch chips in a commercial carbonization plant and from the corresponding raw chips. The activated carbons produced were characterized regarding specific …
Characterization of lignin enforced tannin/furanic foams
2020
Worldwide, tons of lignin is produced annually in pulping plants and it is mainly considered as a waste material. Usually lignin is burned to produce energy for the pulping reactors. The production of value-added materials from renewable materials like lignin, has proved to be challenging. In this study, the effects of addition of three different types of lignin in the production of tannin/furanic foams is investigated. The foams were matured, first at 373 K and finally carbonized at 1073 K and the properties of them including mechanical strength, specific surface area and pore development are investigated before and after thermal treatment. According to the results, higher mechanical stren…